可应用于碳纤维预浸带复合材料、高档不粘锅涂层、化工医药防腐喷涂、3D打印增材制造、环氧树脂增韧剂和碳纤维上浆剂等加工助剂、锂电薄膜等领域,适合静电喷涂、模压成型、SLS增材制造等工艺。
PEKK powder can be used for carbon fiber prepreg,high-grade non-stick pan coating,chemicaland pharmaceutical corrosion resistence coating,3D printing additive manufacturing,epoxyresin toughening agent,carbon fiber sizing agent and other plastic processing additives,lithiumelectric film coating,etc.It is suitable for electrostatic coating,heat-press molding,SLS additivemanufacturing and other processing methods.
PEKK 粉末产品牌号规格表
PEKK powder product series profile
项 目 | 单位 | 测试方法 | CC 5601-50/20 | CC 5801-50/20 |
一般性能 General performance | ||||
密度 Density | g/cm³ | ASTM D792 | 1.28 | 1.28 |
熔融指数 MFR@380℃,5Kg | g/10min | ISO 1133 | ≥80 | 30-50 |
机械性能 Mechanical properties | ||||
拉伸强度 Tensile strength | MPa | ASTM D638 | 90 | 90 |
拉伸模量 Tensile modulus | GPa | ASTM D638 | 3.1 | 3.1 |
断裂伸长率 Elongation at break | % | ASTM D638 | ≥100 | ≥200 |
弯曲强度 Flexural strength | MPa | ASTM D790 | 120 | 120 |
弯曲模量 Flexural sodulus | GPa | ASTM D790 | 2.5 | 2.5 |
热性能 Thermal performance | ||||
玻璃化转变温度 | ℃ | DSC | 155 | 155 |
熔融温度 Meltingtemperature(Tm) | ℃ | DSC | 305 | 305 |
以上规格仅为部分典型规格牌号,KSTONE 有能力提供更多适合市场及客户需求的等级。具体信息请咨询产品经理。
suitable for the needs of market and customer.Please consult the product manager for details.
▶静电喷涂工艺指导
Electrostatic coating processing guide
产品编码 Product Code | 5601-50/20 |
粒径 Particle size(D50,μm) | 50/20 |
1.清除制件表面的所有锐边和毛刺,防止涂层产生针孔等缺陷。 | |
2.首先用表面处理剂或者高温对金属制件进行脱脂除油,然后用干净的氧化铝砂对制件表面进行喷砂处理。 | |
3.清洁处理过的基材必须加热至320~350℃并保持约1小时,然后进行粉末喷涂,将粉末均匀涂覆在制件表面,并在320~350℃温度下烘烤成膜。每层涂层的喷涂时间应控制在10分钟内,如果表面沉积白色未熔粉末,则须停止该区域的粉末喷涂操作,工件温度不得低于320℃。 | |
4.重复上述步骤3,直到达到目标厚度,最后冷却成膜。 | |
5.进行质量检测,最后入库待运。 |
■以上数据为产品的典型数值,不能作为产品验收标准。
The above data are typical values of products and cannot be used as product acceptance criteria.
■最终制品会受到工况等各种因素的影响,产品介绍所示的数值不能保证完全适用于客户的使用条件,应用时请客户做出最终判断。
The final product will be affected by various factors such as working conditions.The values shown in the product introduction
可以用于薄膜、型材、纤维、共混改性、增材制造,适合挤出成型、注塑成型、3D打印等工艺。
PEKK pellet can be uesd for film,stockshape,fiber,filament,compounding,additivemanufacturing,and suitable for extrusion molding,injection molding,3D plprinting and otherprocessing methods.
PEKK颗粒产品牌号规格表
PEKK pellet product series profile
项 目 | 单位 | 测试方法 | FP-7802UN00 | FP-7802GL30 | FP-7802CA30 | FP-5801UNO0 |
一般性能General performance | ||||||
密度Density | g/cm | ASTM D792 | 1.29 | 1.52 | 1.42 | 1.28 |
熔融指数MFR@380℃,5Kg | g/10min | ISO 1133 | 35 | 15 | 6 | 30-50 |
机械性能Mechanical properties | ||||||
拉伸强度Tensile strength | MPa | ASTM D638 | 105 | 185 | 245 | 90 |
拉伸模量Tensile modulus | GPa | ASTM D638 | 4.0 | 12.8 | 24.9 | 3.1 |
断裂伸长率Elongation at break | % | ASTM D638 | 20 | 2.1 | 1.5 | ≥200 |
弯曲强度Flexural strength | MPa | ASTM D790 | 170 | 260 | 353 | 120 |
弯曲模量Flexural modulus | GPa | ASTM D790 | 3.8 | 9.0 | 16.4 | 2.5 |
热性能Thermal performance | ||||||
玻璃化转变温度(Tg | ℃ | DSC | 160 | 160 | 160 | 155 |
熔融温度Melting temperature(Tm) | ℃ | DSC | 350 | 350 | 350 | 305 |
■以上规格仅为部分典型规格牌号, KSTONE 有能力提供更多适合市场及客户需求的等级。具体信息请咨询产品经理
The above specifications are only some typical specifications and brands.KSTONE has the ability to provide more grades
suitable for the needs of market and customer.Please consult the product manager for details
▶注塑工艺指导
Injection molding processing guide
成型参数 | 产品编码 | PEKK FP-7802UN00 |
干燥温度 | Drying temperature ℃ | 150 |
干燥时间 | Drying time(H) | 4 |
喷嘴温度 | Nozzle temperature℃ | 390~380 |
四区温度 | Zone 4 ℃ | 390~380 |
三区温度 | Zone 3 ℃ | 385~365 |
二区温度 | Zone 2 ℃ | 370~350 |
一区温度 | Zone1 ℃ | 355~345 |
模具温度 | Molding Temp.℃ | 210~190 |
■以上数据为产品的典型数值,不能作为产品验收标准。
The above data are typical values of products and cannot be used as product acceptance criteria.
■最终制品会受到工况等各种因素的影响,产品介绍所示的数值不能保证完全适用于客户的使用条件,应用时请客户做出最终判断。
The final product will be affected by various factors such as working conditions.The values shown in the product introduction can not be guaranteed to be fully applicable to the customer's conditions.Please make final judgment when applying.
本公司采用国内独家生产的PEKK树脂,配合美国杜邦、日本大金、旭硝子等国际大品牌氟树脂原料,配备先进智能气流粉碎机组、高速混合机和智能数控研磨机等先进加工设备,质量可靠,并可针对特定工况及应用领域定制工艺配方,可适用于烘焙烤具、塑料模具、汽车配件、医疗手术用具等,广泛应用于食品加工、工业模具、化工医药器械、电子电器、汽车机械、航空航天等耐高温防腐耐磨不沾应用领域。
■KSTONEWT/ST-530是经过PEKK特别改性的特氟龙液体涂料,特别适合工业用高温防腐不沾耐磨涂层应用,无需任何底漆粘结,与金属基材的结合力即可非常强劲,同时表面硬度优于普通特氟龙涂层,表面硬度高,耐磨耐刮擦,且涂层经久耐用,耐高温,耐真空,适用于温度不超过180℃的干式真空泵、工业器具不沾涂层等领域。
■SP/WP-5100为ETFE粉末涂料用底漆,作为金属基体和ETFE涂层的过渡层,可显著提升ETFE与金属的粘合性,使ETFE涂层可在其耐受温度下承受极限真空,适用于温度不超过150℃的反应釜、换热器等化工医药器械、电子电器、汽车机械、航空航天等高耐温重防腐领域。
■SP/WP-5600/5601为PFA粉末涂料用底漆,WP-5600、WP5601分别对应PFA薄涂和厚涂型,作为金属基体和PFA涂层的过渡层,可显著提升PFA与金属的粘合性,使PFA涂层可在其耐受温度下承受极限真空,适用于温度不超过200℃的反应釜、换热器等化工医药器械、电子电器、汽车机械、航空航天等高耐温重防腐领域。
> PEKK喷涂系列产品
PEKK coating product series profile
产品系列 | 涂层类型 | 最高适用温度 | 厚度 | 话用工况及应用领过 |
WT/ST 530 | 单层轻防腐 | 200 | 50~200 | 干式真空泵、锯片、剪切机、园林剪、汽车紧固件,船用螺旋桨、工业烤盘、输送机、燃料喷射器、咖啡盘加热器、食品加工刀具、压缩机鼓风机等风机叶片和底座。 |
SP/WP_ | 多层重防腐 | 150 | 200~1000 | 反应釜、换热器、冷凝器、储罐衬里、离心机、泵机等化工医药生产设备,电子行业酸气管道。 |
SP/WP- | 多层防腐不沾 | 180 | 200~1000 | 搅拌罐、搅拌桨、阀门、泵机等化工医药设备,生物医疗设备、鞋模、纺织品干燥机、食品加工设备。 |
SP/WP- | 多层重防腐 | 200 | 200~1000 | 蒸馏塔、蒸发器、换热器、反应釜、搅拌桨、冷凝器、储罐,离心机等化工医药设备,有机硅晶片生产设备,复印机打印机辊筒、特种灯泡、玻璃,食品加工设备。 |
喷涂工件制作要求
Coating workpiece production requirements
工件加工完进行去翻边、去毛刺,磨圆所有尖锐边缘,建议最小半径6mm,确保工件表面平滑,焊缝需满焊,焊缝处丰满圆滑,无气孔、变形、沙眼、盲孔等缺陷,无尖锐突起、凹坑,所有转角R≥6